| مواد: | سبيكة 52 | نوع من المواد: | سبائك دقيقة |
|---|---|---|---|
| قطر الدائرة: | 0.05 مم ~ 10 مم | صفقة: | بكرة وملف |
| وزن اللفة: | 5 ~ 50 كجم | اسم شائع: | FeNi52 |
| تطبيق: | ختم المعدن الزجاجي | كيمياء: | Fe ، سبيكة ني |
| نوع السبيكة: | سبائك التوسع | ||
| إبراز: | أسلاك الختم الزجاجية 52H,0سلك الختم الزجاجي ذو الـ.8 ملم,0سلك إغلاق زجاجي بقوة 5 ملم,0.8mm Glass Sealing Wire,0.5mm Glass Sealing Wire |
||
52H Glass Sealing52 Vacodil 520 Wire 0.5mm and 0.8mm large in stock with fast delivery
Product Description
The iron-nickel fixed expansion alloy is a series of fixed expansion alloys that can be matched with soft glass and ceramics with different expansion coefficients in a given temperature range by adjusting the nickel content. The expansion coefficient and Curie point increase with the increase of nickel content. This combination gold is a widely used sealing structure material in the electric vacuum industry
Chemical Composition
| Grade | C% | P% | S% | Mn% | Si% | Cu% | Cr% | Mo% | Ni% | Co% | Fe% |
| Alloy52 | Max 0.05 | Max 0.020 | Max 0.020 | Max 0.80 | Max 0.30 | / | / | / | 51.5~52.5 | / | Bal. |
Specifications
| Grade | Common Name | Common Name |
| Alloy52 | Vacodil520 | NILO 52 |
Physical Properties
| Grade | Density | Resistivity |
| Alloy52 | 8.25 g/cm3 | 0.43 |
Grain size of Alloy52
The grain size of the alloy deep-drawing belt should not be less than level 7, and the grain size less than level 7 should not exceed 10% of the area. When the average grain size of the strip with a thickness of less than 0.13mm is estimated, the number of grains along the thickness of the strip should be no less than 8.
Welding performance of Alloy52
The combined gold has good welding performance and can be brazed and spot welded. The combination of gold and soft glass should be pre-oxidized before sealing.
Coefficient of Expansion
| Alloy | Linear Coefficient of Thermal Expansion a,10-6/°C | |||||||
| 20-200°C | 20-300°C | 20-350°C | 20-450°C | 20-500°C | 20-600°C | 20-700°C | 20-800°C | |
| Kovar | 10.4 | 10.2 | 10.3 | 10.3 | 10.3 | 10.8 | / | / |
Heat Treatment For Alloy52
(1) Stress relief annealing In order to eliminate the residual stress of parts after machining, stress relief annealing is required: 430~540℃, heat preservation 1~2h, furnace cooling or air cooling. [1]
(2) Intermediate annealing In order to eliminate the work hardening phenomenon caused by the alloy in the process of cold rolling, cold drawing and cold stamping, in order to facilitate the continued processing. The workpiece needs to be heated to 700~800℃ in a vacuum or protective atmosphere for 30~60min, then furnace cooled, air cooled or water quenched.
(3) Pre-oxidation treatment When the combined gold is used as a sealing material, it should be pre-oxidized before sealing. A uniform and dense oxide film is formed on the surface of the alloy. The parts are heated in saturated wet hydrogen at 1100°C for 30 minutes, and then oxidized in the air at about 800°C for 5-10 minutes. The weight gain of the parts should be 0.1~0.3mg/cm2
Company Profile
Customer Photos
Exhibition
Production Process
Testing Equirement
Shipment
Contact Us
تفاصيل الاتصال
Ohmalloy Material Co.,Ltd
اتصل شخص: Jully
الهاتف :: +8617301602658
إرسال استفسارك مباشرة لنا
أكثر سبائك الدقة
-
سبائك مغناطيسية دقيقة 3J53 دقيقة تشبه Ni Span C
-
Invar36 FeNi36 الدقة الأنابيب الشعرية الشعرية المستخدمة في صناعة الأدوية
-
أعلى جودة مخزون جاهز من Kovar Tube / Pipe 4J29 / 29HK Tube
-
توسيع ني ني شركة سبائك سلك Ni33Co17 لختم ومطابقة السيراميك
-
فراغ فرن نيكل مقرها سبائك للزجاج إلى المعادن ختم فراغ تبديل أنبوب
-
سلك الروديوم الحراري البلاتيني نوع S/R/B